Zc-MMMCCXLI Silanene xlpe Nigrum Vallis compositis ad aeria insulated funem usque ad 10kv
est a se-gradus Silanene Polyethylene insulating materiam, a crosslinking polyethylene materia paratus per specialem processus, usura summus qualitas polyethylene resinae, silane, utendo summus qualitas Polyethylene resinae, silane, per altum qualis polyethylene resinae, silane, utendo summus qualitas Polyethylene resinae, Silanene Igitur, initiat, Catalyst, Antioxidant et aliis additives. Est usus est in Aerial Insulated funem usque ad X kv. Hoc est optimum extrusionem perficientur, firmum & certa corporis et eget Indicatores.
| Productio | Silanene xlpe tecta
componit |
| Product Code | 3241 |
| Descriptio | Monosil 10kv |
| Vexillum | Test modus |
|
| Density (G / CM³) | ASTM D792 | 0.92 ± 0.01 |
| Tensile fortitudo (MPa) | IEC 60811-1-1 | 18.5 |
| Elongatio ad confractus (%) | 510 |
| Mfi 2.16kg & 190ºC (G / 10min) | ASTM D1238 |
|
| Senex | Tensile vires variation (%) | 60811-1-2 IEC | V |
| Elongatio variation (%) | -6 |
| Hot Set @ 200ºC 15min, 0.2MPA | Elongatio sub onus (%) | IEC 60811-2-1 | 50 |
| Permanent deformatio post refrigerationem (%) | -3 |
| Gel content (%) | ASTM D2765 |
|
| Minimum temperatus morsu @ -76ºC | ASTM D746 | (0/30) Transite |
| Volubilis resistentia (ω · cm) | IEC (LX) XCIII | 5x1014 |
| DieLectric fortitudinem (Mv / M) | 60243-1 IEC | 37 |
| 60ºC luxuriae factor, 50Hz | IEC (LX) CCL | 2x10-4 |
| Dielectric constant 20ºC, 50Hz | IEC (LX) CCL | 1.7 |
Typical values in mensa sunt mensus sub conditione, quod materia est plene crosslinked, et si salficiente crosslinking non effectum, in perficientur de materia sit alia.
Processing:
quod est commendatur ad conventional extruder (tres-layer co-extrusionem longitudinem, diameter Ratio XX: I ad XXX, I), quia operatio, et alia apparatu necessitates ad adaequatum secundum situ.
| Zona | Pascens | Section compressionem | Homogenization sectioni | Section |
| Temperatus rangeºC | 160-180 | 180-200 | 200-210 | 210-220 |
- supra temperatus est tantum pro reference. Est suadetur ut mos adjust secundum temperatus imperium suae respective apparatu, in current tempore extrusionis, et liquescens pressura et ipsa situ post funem extrusionem.