ZC-5832 Irradiation Crosslinking LSZH Compounds for Automotive HV cables
These materials use superior quality polar resin, elastomer resin, rubber and grafting material as the base materials, adding antioxidants, anti-ultraviolet agents, lubricants, flame retardants and other additives, mixed and granulated. They have excellent solvent resistance property ; excellent flame retardant property and it can
pass the single vertical combustion test (ISO 19642 standard); They have good tear resistance property and good long-term aging performance as well as excellent high temperature resistance property.
Standard: ISo 6722
Application: Manufacture of high-voltage electrical system cables inside new energy vehicles such as pure electric, hybrid,and fuel cell.
Characteristic: Minimum controllable hardness≤80A
| (Irradiation / E-beam) HFFR / LSZH |
| Automotive Wire |
| Product code | 5832 |
| Standards | Test method | ISO 6722
QC/T 1037-2016 |
| Tensile strength (Mpa) | IEC 60811-1-1 | 10.5 |
| Elongation at break (%) | 350 |
| Thermal aging | Test condition (ºC'h) | IEC60811-1-2 | 170'240 |
| Tensile strength variation (%) | -10 |
| Breaking elongatior variation (%) | -18 |
| Thermal shock (150ºC'5kg'1h) |
| No cracking |
| Low temperature performance (ºC) |
| -40 |
| Hot set @200ºC 15min, 0.2Mpa | Elongation inder the load (%) | IEC 60811-2-1 | 11 |
| Permanent deformation after cooling (%) | 0 |
| High temperature pressure test | Test condition (ºC'h) |
| 150'4 |
| Indentation depth (%) |
| 14 |
| Thermal shrinkage @130ºC, 1h(%) |
| 1.1 |
| Volume resistivity @20ºC (Ω*cm) | ASTM D257 | 2.0×1014 |
| Dielectric strength @20ºC (MV/m) | IEC 60263-1 | 16 |
| Smoke density | Flame |
|
|
| Flameless |
|
|
| Oxygen index (%) |
|
|
| Abrasion esistance test |
|
|
| Corrosion test | pH |
| 5.8 |
| Electrica onductivity (μs/mm) |
| 1.5 |
| Halogen acid gas content (mg/g) |
| 0 |
| Toxicity Index |
| 1.1 |
-The data in the table are typical and should not be considered as specification limits or separately applied design data.