ZC-5101 Thermoplastic LSZH Flame Retardant polyolefin Cable Compounds [90ºC]
These products are thermoplastic low-smoke halogen-free flame retardant polyolefin insulation materials or sheath materials. They are based on polyolefin as the matrix, adding inorganic flame retardants, compatibilizers, lubricants, antioxidants and other additives through continuous mixing and plasticization granulation. The production process is continuous. The materials have good extrusion processing performance, mechanical properties and stable&reliable flame retardant performance.Typical values in the table are measured under the condition that the material is fully crosslinked, and if suficient crosslinking is not achieved, the performance of the material may be different.
| (Thermoplastic & Irradiation/E-beam & UV Irradiation) HFFR / LSZH |
|
|
| Thermoplastic |
| Product code | 5101 |
| Standards | Test method | GB/T 32129-2015 |
| Density (g/cm³) | ASTM D792 |
|
| Tensile trength (Mpa) | IEC 60811-1-1 | 12 |
| Elongation at break (%) | 200 |
| Thermal aging | ºC'h |
| 100'168 |
Tensile strength
variation(%) | 10 |
Breaking elongation
variation (%) | -10 |
| Thermal deformation @90ºC, 4H (%) |
| 31 |
| Thermal shock (150ºC'5kg'1h) |
| No cracking |
| Impact brittlenes (-25ºC) Failure(Piece) | IEC 60811-1-4 | 0/30 |
| Hot set @200ºC 15min, 0.2Mpa | Elongation under the load (%) | IEC 60811-2-1 |
|
Permanent
deformation after cooling (%) |
|
| Volume resistivity @20ºC (Ω·cm) | ASTM D257 | 6×10¹³ |
| Dielectric strength @20ºC (MV/m) |
| 26 |
| Smoke density | Flame |
| 60 |
| Flameless |
| 200 |
| Fluorine content (%) |
|
|
| Oxygen index (%) |
| 32 |
| Corosion test | pH |
| 5 |
Electrical
conductivity
(μs/mm) |
| 3 |
| Halogen acid gas content (mg/g) |
| 3 |