The product is crosslinkable modified polyethylene insulating material,selected high-quality polyethylene resin, added auxiliary materials Dicumyl peroxide and antioxidants. The process focuses on the addition of auxiliary materials and the uniformity of mixing, and make sure the production process clean & pollution-free. The product is used for 10kV crosslinking polyethylene cable insulation layer, with the stable and reliable physical & chemical indicator, and excellent processing performance.
Property:
(
Typical values in the table are measured under the condition that the material is fully crosslinked,and if sufficient crosslinking is not achieved, the performance of the material may be different.
Processing:
It is recommended to use a conventional extruder (three-layer co-extrusion, length-diameter ratio of 20:1 to 30:1) for operation, and other equipment needs to be adjusted according to the situation.
-Above temperature is only for reference. It is recommended that customers adjust according to the current at the time of extrusion, the melting pressure and the actual situation after the cable extrusion. This process proposal is not intended as terms of cooperation between the parties.
Product packing
Cartons packaged with pallets and films, N.W:600 kg/Carton.
(Cartons are sealed and packaged, with pallets at the bottom of the box, lined with polyethylene film protection. )
Note:
1. Before using, it is necessary to confirm that the package is not damaged, and if the product particles are found to be contaminated or discolored, stop using.
2. Transportation, stacking and storage should prevent sun, rain and water immersion, etc., and the storage environment should be clean, dry and ventilated.
3. The best using period is within six months from the date of manufacture.
4. According to industry experience, it is recommended that the extruder be equipped with a filter screen, which can strengthen plasticization and stabilize the current.