The materials is a kind of peroxide crosslinking polyethylene insulating materials with water-tree retardant performance,which is improved insulating materials developed for the water-tree resistant requirements of wire and cable.The materials also has water-tree resistant performance on the basis of excellent processing performance of general peroxide crosslinking materials.
Typical values in the table are measured under the condition that the material is fully crosslinked,and if sufficient crosslinking is not achieved, the performance of the material may be different.
It is recommended to use a conventional extruder (three-layer co-extrusion, length-diameter ratio of 20:1 to 30:1) for operation, and other equipment needs to be adjusted according to the situation.
-Above temperature is only for reference.As the using conditions are not within our control,it is recommended that customers adjust according to the current at the time of extrusion,the melting pressure and the actual situation after the cable extrusion.
Cartons packaged with pallets and films, N.W:600 kg/Carton.
(Cartons are sealed and packaged, with pallets at the bottom of the box, lined with polyethylene film protection. )
1. Before using, it is necessary to confirm that the package is not damaged, and if the product particles are found to be contaminated or discolored, stop using.
2. Transportation, stacking and storage should prevent sun, rain and water immersion, etc., and the storage environment should be clean, dry and ventilated.
3. The best using period is within six months from the date of manufacture.