Zc-5327 Irradiation Crosslinking LSZH Compounds for Photovoltaic Cable (125 º C] sheath
These are halogen free flame retardant wire and cable materials, which are made of high-quality resins, flame retardants, antioxidants and lubricants, mixed and granulated. These materials do not contain halogens, do not release toxic gases when burning, have superior flame retardant properties, physical & mechanical properties
and good processing properties. Temperature resistance grade is 125C.
Standard: EN50618-2014/UL4703-2014
| (Thermoplastic & Irradiation/E-beam & UV Irradiation) HFFR / LSZH |
| Photovoltaic |
| Product code | 5327 |
| Standards | Test method | EN 50618-2014,
UL 4703-2014 |
| Density (g/cm³) | ASTM D792 | 1.44 |
| Tensile trength (Mpa) | IEC 60811-1-1 | 12 |
| Elongation at break (%) | 170 |
| Thermal aging | ºC'h |
| 150'168 |
| Tensile strength variation(%) | -15 |
| Breaking elongation variation (%) | -23 |
| Thermal shock (150ºC'5kg'1h) |
| No cracking |
| Impact brittlenes (-25ºC) Failure(Piece) | IEC 60811-1-4 |
|
| Hot set @200ºC 15min, 0.2Mpa | Elongation under the load (%) | IEC 60811-2-1 | 30 |
| Permanent deformation after cooling (%) | 3 |
| Volume resistivity @20ºC (Ω·cm) | ASTM D257 | 31.0×1013 |
| Dielectric strength @20ºC (MV/m) |
| 330 |
| Fluorine content (%) |
| 0 |
| Oxygen index (%) |
| 333 |
| Corosion test | pH |
| 5.5 |
| Electrical conductivity (μs/mm) |
| 1.4 |
| Halogen acid gas content (mg/g) |
| 0 |
-The data in the table are typical and should not be considered as specification limits or separately applied design data.