Zc-5327 Irradiation Crosslinking LSZH Compounds for Photovoltaic Cable (125 º C] sheath
These are halogen free flame retardant wire and cable materials, which are made of high-quality resins, flame retardants, antioxidants and lubricants, mixed and granulated. These materials do not contain halogens, do not release toxic gases when burning, have superior flame retardant Properties, & corporalis mechanica proprietatibus
et bonum dispensando proprietatibus. Temperature resistentia gradu est 125c.
Latin: en50618-2014 / Ul4703-2014
| (Thermoplastic & irradiatio / E-trabem & UV irradiatio) Hffr / lszh |
| Photovoltaic |
| Product Code | 5327 |
| Signa | Test modus | En 50618-2014,
Ul 4703-2014 |
| Density (G / CM³) | ASTM D792 | 1.44 |
| TRENSILIS Tresgth (MPA) | IEC 60811-1-1 | 12 |
| Elongatio ad confractus (%) | 170 |
| Scelerisque senescentis | ºc'h |
| 150'168 |
| Tensile vires variation (%) | -15 |
| Effrego elongatio variation (%) | -23 |
| Scelerisque inpulsa (150ºC'5KG'1H) |
| Nulla fregisset |
| Impulsum Brittlenes (-25ºC) Defectum (Piece) | 60811-1-4 IEC |
|
| Hot Set @ 200ºC 15min, 0.2MPA | Elongatio sub onus (%) | IEC 60811-2-1 | 30 |
| Permanent deformatio post refrigerationem (%) | 3 |
| Volubilis resistentia @ 20ºC (ω · cm) | Astm d257 | 31.0 × MXIII |
| Dielectric Fortitudo @ 20ºC (MV / M) |
| 330 |
| Fluorine content (%) |
| 0 |
| Index oxygeni (%) |
| 333 |
| Corosion test | pH |
| 5.5 |
| Conductors Electrical (μs / mm) |
| 1.4 |
| Halogen Acidum Gas content (mg / g) |
| 0 |
Id notitia in mensa sunt typical et non potest considerari ut specificationem fines vel seorsim applicari consilio data.