It is a two-step silane polyethylene insulating material,using high-quality polyethylene resin,adding imported silane coupling agent and initiator to prepare grafted polyethylene (material A),and using high-quality imported organotin catalyst,antioxidant,etc.to prepare catalytic masterbatch(material B).The production uses industry-leading loss-in-weight scales and Extruders cum uniformis et stabilis formulae et reliable processes.it adhibetur ad insulating layer of xlpe funem usque ad 3kv, insulated est optimum extrusionem perficientur, firmum est ad 10kv.it et excelsum superficie metam, firmum & certa corporis et chemical Indicatores.
Property:
Typical values in mensa sunt mensus sub condicionem quod materia est plene crosslinked, et si sufficiens crosslinking non effectum, in perficientur de materia sit alia.
Processing:
Est suadetur ut in speciali extruder pro Polyethylene ad dispensando (Longitudo-diameter Ratio XVIII: I TO25: I), et alia apparatu necessitates ad adaequatum secundum situ.
-Above temperatus est tantum pro reference.it est suadetur quod customers adjust secundum temperatus imperium suae respective apparatu, ad tempus extrusionem, et liquescens pressura et ipsa situ post funem extrusionem. Suscitavit aequabiliter materiae et b oportet excituit aequaliter ante pascens, ita ut uniformitatem calidae aqua crosslinking.
Product sarcina
Vacuum sarcina in aluminium ffoyle sacculos. NW de materia A (23.75 ± 0.05) kg / peram, NW de materia B (1.25 ± 0.005) kg / peram.
Nota:
1.The mixtisque debet esse in VIII horas post MIXING.The Ratio materiae ad materiam B est XCV: 5.If sarcina of materia est rumpitur, velit non utor.polyethylene masterbatch potest esse in processus (postulo ut arida, humorem content <200ppm)
2.Transportation, Stacking et repono ne sol, pluvia et aqua immersionem, etc et repono environment mundare, sicca et ventilari.
3.The optimus usura tempus est intra sex menses a date de fabricantibus.