Zhongchao
Aquam lignum retardant xlpe tincidunt particula ad MV funem usque 35kv
Quod productum est crosslinkable modified polyethylene insulating materia, lectus summus qualitas polyethylene resina. In processus focuses in additionem auxiliariariaterials et uniformitatem miscentium et fac productio processus mundus & pollutio-liberum. Thepoduct est usus 10kv crosslinking polyethylene funem velit layer, cum firmum et certa corporis 8chemical indicator et praeclarus processus perficientur.
| Productio | Peroxide xlpe tecta componit | ||
| Product Code | 3112 | ||
| Descriptio | 35kv | ||
| Vexillum | Test modus | ||
| Density (g / cm³) | ASTM D792 | ||
| Tensile fortitudo (MPa) | IEC 60811-1-1 | ≥16 | |
| Elongatio ad confractus (%) | ≥400 | ||
| Mfi 2.16kg & 190ºC (G / 10min) | ASTM D1238 | ||
| Senex | Tensile vires variation (%) | 60811-1-2 IEC | ≤ ± XX |
| Elongatio variation (%) | ≤ ± XX | ||
| Hot Set @ 200ºC 15min, 0.2MPA | Elongatio sub onus (%) | IEC 60811-2-1 | ≤80 |
| Permanent deformatio post refrigerationem (%) | ≤5 | ||
| Gel content (%) | ASTM D2765 | ≥80 | |
| Minimum temperatus morsu @ -76ºC | ASTM D746 | (0/30) Transite | |
| Volubilis resistentia (ω · cm) | IEC (LX) XCIII | ≥1x1014 | |
| DieLectric fortitudinem (Mv / M) | 60243-1 IEC | ≥25 | |
| 60ºC luxuriae factor, 50Hz | IEC (LX) CCL | ≤5x10-4 | |
| Dielectric constant 20ºC, 50Hz | IEC (LX) CCL | ≤2.35 | |
Typical values in mensa sunt mensus sub conditione, quod materia est plene crosslinked, et si salficiente crosslinking non effectum, in perficientur de materia sit alia.
Nanjing Zhongchao nova materiae corporation est ducens polyolefin componit manufacturer in virtute et telecommunication industria cum sua instauratione in MMXI. Nos garnered clients worldwide nostrae internation. Nostra commitment ut viridi innovation et tradens client prodest agitet nostra metam esse Sinis scriptor summo provisor de polyolefin et polyethylene componit. Omnibus nostris aestimantur clients, ut bene receperint te visitare Zhongchao et testimonium firsthand excellentiam nostri summus qualitas componit et solutions.